{"_buckets": {"deposit": "168d0230-3d58-4b23-9dad-ccc0c60855e7"}, "_deposit": {"created_by": 3, "id": "10002", "owners": [3], "pid": {"revision_id": 0, "type": "depid", "value": "10002"}, "status": "published"}, "_oai": {"id": "oai:nifs-repository.repo.nii.ac.jp:00010002", "sets": ["32"]}, "author_link": ["62066", "62067", "62068", "62071", "62069", "62070", "62072"], "item_5_biblio_info_7": {"attribute_name": "書誌情報", "attribute_value_mlt": [{"bibliographicIssueDates": {"bibliographicIssueDate": "2008-10-01", "bibliographicIssueDateType": "Issued"}, "bibliographic_titles": [{}, {"bibliographic_title": "Research Report NIFS-Series", "bibliographic_titleLang": "en"}]}]}, "item_5_description_5": {"attribute_name": "抄録", "attribute_value_mlt": [{"subitem_description": "\"The compatibility of Reduced Activation Ferritic/Martensitic Steel (RAFM) with liquid Li and molten-salt Flibe have been characterized and accessed. Static compatibility tests were carried out in which the specimens were immersed into liquid Li or Flibe in isothermal autoclaves. Also carried out were compatibility tests in flowing liquid Li by thermal convection loops. In the case of liquid Li, the corrosion rate increased with temperature significantly. The corrosion was almost one order larger for the loop tests than for the static tests. Chemical analysis showed that the corrosion was enhanced when the level of N in Li is increased. Transformation from martensitic to ferritic phase and the resulting softening were observed in near-surface area of Li-exposed specimens, which were shown to be induced by decarburization. In the case of Flibe, the corrosion loss was much larger in a Ni crucible than in a RAFM crucible. Both fluorides and oxides were observed on the surfaces. Thus, the key corrosion process of Flibe is the competing process of fluoridation and oxidation. Possible mechanism of the enhanced corrosion in Ni crucible is electrochemical circuit effect. It was suggested that the corrosion loss rate of RAFM by liquid Li and Flibe can be reduced by reducing the level of impurity N in Li and avoiding the use of dissimilar materials in Flibe, respectively.\"", "subitem_description_type": "Abstract"}]}, "item_5_source_id_10": {"attribute_name": "ISSN", "attribute_value_mlt": [{"subitem_source_identifier": "0915-633X", "subitem_source_identifier_type": "ISSN"}]}, "item_5_text_25": {"attribute_name": "登録情報", "attribute_value_mlt": [{"subitem_text_value": "Made available in DSpace on 2010-02-05T10:17:11Z (GMT). No. of bitstreams: 0\n Previous issue date: 2008-10"}]}, "item_5_text_8": {"attribute_name": "報告書番号", "attribute_value_mlt": [{"subitem_text_value": "NIFS-924"}]}, "item_access_right": {"attribute_name": "アクセス権", "attribute_value_mlt": [{"subitem_access_right": "metadata only access", "subitem_access_right_uri": "http://purl.org/coar/access_right/c_14cb"}]}, "item_creator": {"attribute_name": "著者", "attribute_type": "creator", "attribute_value_mlt": [{"creatorNames": [{"creatorName": "\"Muroga, T.", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "62066", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Nagasaka, T.", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "62067", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Kondo, M.", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "62068", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Sagara, A.", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "62069", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Noda, N.", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "62070", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Suzuki, A.", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "62071", "nameIdentifierScheme": "WEKO"}]}, {"creatorNames": [{"creatorName": "Terai, T.\"", "creatorNameLang": "en"}], "nameIdentifiers": [{"nameIdentifier": "62072", "nameIdentifierScheme": "WEKO"}]}]}, "item_language": {"attribute_name": "言語", "attribute_value_mlt": [{"subitem_language": "eng"}]}, "item_resource_type": {"attribute_name": "資源タイプ", "attribute_value_mlt": [{"resourcetype": "research report", "resourceuri": "http://purl.org/coar/resource_type/c_18ws"}]}, "item_title": "Compatibility of Reduced Activation Ferritic/Martensitic Steels with Liquid Breeders", "item_titles": {"attribute_name": "タイトル", "attribute_value_mlt": [{"subitem_title": "Compatibility of Reduced Activation Ferritic/Martensitic Steels with Liquid Breeders", "subitem_title_language": "en"}]}, "item_type_id": "5", "owner": "3", "path": ["32"], "permalink_uri": "http://hdl.handle.net/10655/2578", "pubdate": {"attribute_name": "公開日", "attribute_value": "2010-02-05"}, "publish_date": "2010-02-05", "publish_status": "0", "recid": "10002", "relation": {}, "relation_version_is_last": true, "title": ["Compatibility of Reduced Activation Ferritic/Martensitic Steels with Liquid Breeders"], "weko_shared_id": -1}
Compatibility of Reduced Activation Ferritic/Martensitic Steels with Liquid Breeders
http://hdl.handle.net/10655/2578
http://hdl.handle.net/10655/2578cea27a5f-64e2-4a4b-87de-7ea5d9fe378e
Item type | 研究報告書 / Research Paper(1) | |||||
---|---|---|---|---|---|---|
公開日 | 2010-02-05 | |||||
タイトル | ||||||
言語 | en | |||||
タイトル | Compatibility of Reduced Activation Ferritic/Martensitic Steels with Liquid Breeders | |||||
言語 | ||||||
言語 | eng | |||||
資源タイプ | ||||||
資源タイプ識別子 | http://purl.org/coar/resource_type/c_18ws | |||||
資源タイプ | research report | |||||
アクセス権 | ||||||
アクセス権 | metadata only access | |||||
アクセス権URI | http://purl.org/coar/access_right/c_14cb | |||||
著者 |
"Muroga, T.
× "Muroga, T.× Nagasaka, T.× Kondo, M.× Sagara, A.× Noda, N.× Suzuki, A.× Terai, T." |
|||||
抄録 | ||||||
内容記述タイプ | Abstract | |||||
内容記述 | "The compatibility of Reduced Activation Ferritic/Martensitic Steel (RAFM) with liquid Li and molten-salt Flibe have been characterized and accessed. Static compatibility tests were carried out in which the specimens were immersed into liquid Li or Flibe in isothermal autoclaves. Also carried out were compatibility tests in flowing liquid Li by thermal convection loops. In the case of liquid Li, the corrosion rate increased with temperature significantly. The corrosion was almost one order larger for the loop tests than for the static tests. Chemical analysis showed that the corrosion was enhanced when the level of N in Li is increased. Transformation from martensitic to ferritic phase and the resulting softening were observed in near-surface area of Li-exposed specimens, which were shown to be induced by decarburization. In the case of Flibe, the corrosion loss was much larger in a Ni crucible than in a RAFM crucible. Both fluorides and oxides were observed on the surfaces. Thus, the key corrosion process of Flibe is the competing process of fluoridation and oxidation. Possible mechanism of the enhanced corrosion in Ni crucible is electrochemical circuit effect. It was suggested that the corrosion loss rate of RAFM by liquid Li and Flibe can be reduced by reducing the level of impurity N in Li and avoiding the use of dissimilar materials in Flibe, respectively." | |||||
書誌情報 |
en : Research Report NIFS-Series 発行日 2008-10-01 |
|||||
報告書番号 | ||||||
NIFS-924 | ||||||