@article{oai:nifs-repository.repo.nii.ac.jp:00011433,
 author = {FU, Haiying and NAGASAKA,  Takuya and MUROGA,  Takeo and GUAN, Wenhai and NOGAMI, Shuhei and HASEGAWA, Akira and SERIZAWA, Hisashi},
 issue = {Special Issue 2},
 journal = {Plasma and Fusion Research},
 month = {Apr},
 note = {Dissimilar joints between 9Cr-ODS and JLF-1 were fabricated by hot isostatic pressing (HIP) and by electron beam welding (EBW), respectively. Compared to the HIP at 1000 °C, HIP at higher temperatures of 1050 °C and 1100 °C is effective to improve the joining strength of the joints. All the as-HIPed joints fractured at the interface during tensile tests. 1050 °C-HIP showed the best joining strength and reduction of area. Post-weld heat treatment (PWHT) with normalization and tempering (N&T) could further improve the joining properties of the HIPed joints. The joints fractured outside the interface at the JLF-1 base metals. EBW showed better weld-ability than HIP, because the joint made by EBW did not fracture at the weld metal during tensile tests, but always fractured at JLF-1 side. However, the properties of the HIPed joints were improved after PWHT with N&T, and were comparable to that made by EBW.},
 title = {Weldability of 9Cr-ODS and JLF-1 Steels for Dissimilar Joining with Hot Isostatic Pressing and Electron Beam Welding},
 volume = {10},
 year = {2015}
}